Effect of light polarization on holographic recording in glassy azocompounds and chalcogenides

Light polarization effects on a holographic grating recording in a glassy chalcogenide a-As₄₀S₁₅Se₄₅ film has been experimentally studied and compared with previously studied glassy molecular azobenzene film 8a at 633, using s - s,p - p, CE-1 and CE-2 circular-elliptic recording-beam polarizations (differing by light electric field rotation directions). The azocompound exhibited much higher self-diffraction efficiency (SDE) and diffraction efficiency whereas chalcogenide was more sensitive. Their recording efficiency polarization dependences also were different. SDE up to 45% was achieved in 8a with p - p and up to 2. 6% in a-As₄₀S₁₅Se₄₅ with CE-2 polarized recording beams. The polarization changes in the diffraction process were studied as well in these and other materials (11, 16, 19 and a-As₂S₃ film, LiTaO₃:Fe crystal). It was found that light polarization changes in the process of diffraction from gratings recorded vectorially by s-p polarizations depended on chemical composition, wavelength, and exposure time. Vector gratings with SDE up to 25% were recorded in 8a, rotating a linear polarization by 90°. No light polarization changes were found in azobenzene 19 and chalcogenide films and in LiTaO₃:Fe crystal, thus showing a vector recording of scalar holograms. The recording mechanisms in azocompounds and chalcogenides are discussed and compared.