Peculiarities of luminescent properties of cerium doped YAG transparent nanoceramics

Vladimir Pankratov; Liana Shirmane; Tadeusz Chudoba; Piotr Gluchowski; Darek Hreniak; Wieclaw Strek; Witold Lojkowski

doi:10.1016/j.radmeas.2009.12.014

Peculiarities of luminescent properties of cerium doped YAG transparent nanoceramics

Vladimir Pankratov
, Liana Shirmane^*
, Tadeusz Chudoba
, Piotr Gluchowski
, Darek Hreniak
, Wieclaw Strek
, Witold Lojkowski

^*Šī darba korespondējošais autors

Polish Academy of Science
Polish Academy of Sciences

Zinātniskās darbības rezultāts: Devums žurnālam › Zinātniskais raksts (žurnālā) › koleģiāli recenzēts

19 Atsauces (Scopus)

Kopsavilkums

Optical and luminescence properties of transparent nanosized cerium doped Y₃Al₅O₁₂ (YAG:Ce) ceramics have been studied. YAG:Ce nanoceramics were obtained by means of low temperature and high pressure (LTHP) sintering method. Nanoceramic samples were sintered in the 2-8 GPa pressure range, whereas Ce³⁺ concentration was varied in the 0.5-5 at. % range. It is shown that, in contrast to the single crystal, a strong rise of absorption coefficient was detected already at wavelength shorter than 400 nm in all nanoceramic samples studied. Furthermore, in nanoceramic samples unusual UV emission band near 3.1 eV was observed, which is not observed in the YAG:Ce single crystal. High pressure applied during nanoceramics sintering leads to significant changes in their optical and luminescence properties.

Oriģinālvaloda	Angļu
Lapas (no-līdz)	392-394
Žurnāls	Radiation Measurements
Sējums	45
Izdevuma numurs	3-6
DOIs	https://doi.org/10.1016/j.radmeas.2009.12.014
Publikācijas statuss	Publicēts - 2010

OECD Zinātnes nozare

1.3 Fizika un astronomija

Piekļuve Dokumentiem

10.1016/j.radmeas.2009.12.014

Citi faili un saites

Citēt šo

@article{4ea0d2f8c1934f6e8cc1b5eacd9bc948,

title = "Peculiarities of luminescent properties of cerium doped YAG transparent nanoceramics",

abstract = "Optical and luminescence properties of transparent nanosized cerium doped Y3Al5O12 (YAG:Ce) ceramics have been studied. YAG:Ce nanoceramics were obtained by means of low temperature and high pressure (LTHP) sintering method. Nanoceramic samples were sintered in the 2-8 GPa pressure range, whereas Ce3+ concentration was varied in the 0.5-5 at. \% range. It is shown that, in contrast to the single crystal, a strong rise of absorption coefficient was detected already at wavelength shorter than 400 nm in all nanoceramic samples studied. Furthermore, in nanoceramic samples unusual UV emission band near 3.1 eV was observed, which is not observed in the YAG:Ce single crystal. High pressure applied during nanoceramics sintering leads to significant changes in their optical and luminescence properties.",

keywords = "Luminescence, Nanoceramic, Nanocrystals",

author = "Vladimir Pankratov and Liana Shirmane and Tadeusz Chudoba and Piotr Gluchowski and Darek Hreniak and Wieclaw Strek and Witold Lojkowski",

year = "2010",

doi = "10.1016/j.radmeas.2009.12.014",

language = "English",

volume = "45",

pages = "392--394",

journal = "Radiation Measurements",

issn = "1350-4487",

publisher = "Elsevier Ltd",

number = "3-6",

}

TY - JOUR

T1 - Peculiarities of luminescent properties of cerium doped YAG transparent nanoceramics

AU - Pankratov, Vladimir

AU - Shirmane, Liana

AU - Chudoba, Tadeusz

AU - Gluchowski, Piotr

AU - Hreniak, Darek

AU - Strek, Wieclaw

AU - Lojkowski, Witold

PY - 2010

Y1 - 2010

N2 - Optical and luminescence properties of transparent nanosized cerium doped Y3Al5O12 (YAG:Ce) ceramics have been studied. YAG:Ce nanoceramics were obtained by means of low temperature and high pressure (LTHP) sintering method. Nanoceramic samples were sintered in the 2-8 GPa pressure range, whereas Ce3+ concentration was varied in the 0.5-5 at. % range. It is shown that, in contrast to the single crystal, a strong rise of absorption coefficient was detected already at wavelength shorter than 400 nm in all nanoceramic samples studied. Furthermore, in nanoceramic samples unusual UV emission band near 3.1 eV was observed, which is not observed in the YAG:Ce single crystal. High pressure applied during nanoceramics sintering leads to significant changes in their optical and luminescence properties.

AB - Optical and luminescence properties of transparent nanosized cerium doped Y3Al5O12 (YAG:Ce) ceramics have been studied. YAG:Ce nanoceramics were obtained by means of low temperature and high pressure (LTHP) sintering method. Nanoceramic samples were sintered in the 2-8 GPa pressure range, whereas Ce3+ concentration was varied in the 0.5-5 at. % range. It is shown that, in contrast to the single crystal, a strong rise of absorption coefficient was detected already at wavelength shorter than 400 nm in all nanoceramic samples studied. Furthermore, in nanoceramic samples unusual UV emission band near 3.1 eV was observed, which is not observed in the YAG:Ce single crystal. High pressure applied during nanoceramics sintering leads to significant changes in their optical and luminescence properties.

KW - Luminescence

KW - Nanoceramic

KW - Nanocrystals

UR - https://www.scopus.com/pages/publications/77955305224

UR - https://www.sciencedirect.com/science/article/abs/pii/S1350448709003813

U2 - 10.1016/j.radmeas.2009.12.014

DO - 10.1016/j.radmeas.2009.12.014

M3 - Article

AN - SCOPUS:77955305224

SN - 1350-4487

VL - 45

SP - 392

EP - 394

JO - Radiation Measurements

JF - Radiation Measurements

IS - 3-6

ER -

Peculiarities of luminescent properties of cerium doped YAG transparent nanoceramics

Kopsavilkums

OECD Zinātnes nozare

Piekļuve Dokumentiem

Citi faili un saites

Nospiedums

Citēt šo