Phase transitions and upconversion luminescence in oxyfluoride glass ceramics containing Ba4Gd3F17 nanocrystals

Novel transparent Er³⁺ doped oxyfluoride glass-ceramics containing Ba₄Gd₃F₁₇ nanocrystals were prepared by melt quenching followed by heat treatment of as-prepared glasses. The phase composition and microstructure were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Intense upconversion luminescence (UCL) was detected. Longer characteristic decay times and splitting of the luminescence bands compared to the precursor glass indicated the incorporation of erbium ions in the crystalline phase. The spectroscopic properties of glass ceramics were compared with single phase cubic and rhombohedral Ba₄Gd₃F₁₇ ceramics. The unit cell parameters and atomic positions in the rhombohedral phase were calculated using Rietveld refinement. The local environment of Er³⁺ and the phonon energy of both polymorphs were analyzed using luminescence and Raman spectroscopy. In the glass ceramics, a phase transition from distorted metastable fluorite to ordered rhombohedral Ba₄Gd₃F₁₇ was observed and resulted in the enhancement of the efficiency of UCL.