Thermally and optically stimulated radiative processes in LiBaF₃ crystals

In LiBaF₃ crystals both valence-core transitions (5.4-6.5 eV) and so-called self-trapped exciton luminescence (about 4.3 eV) are important for practical application. Here, we present a study of 4.3 eV luminescence under photo- and thermostimulation after X-irradiation of undoped LiBaF₃ crystals at various temperatures. Optically stimulated luminescence as a result of electron recombination with both self-trapped holes and holes localized at some defects, were observed after X-irradiation below 130 K and that of electron recombination with defect-localized holes was observed after X-irradiation above 130 K. The spectra of thermo-stimulated luminescence (TSL) contain a broad band about 4 eV related to the electron (high-energy side) or hole (low-energy side) recombination depending on TSL peak temperature.